Mineral Wool
Non-combustibility, sound absorption, insulation performance, A-CLASS
. . .
This product is an inorganic artificial mineral fiber insulation produced by melting calcium silicate ores or slag at a high temperature of
about 1500 ℃, making them fiber using high-speed torque and shaping them a certain form through a binder.
It is applied to A-Class fireproof structures to prevent fire spread in the vessel and acquired official certifications from the
classification societies of many countries including European countries.
| Division | Performance | Test Method | ||
|---|---|---|---|---|
| Hot shrinkage temperature | Over 600℃ (10% contraction of thickness) | KS L 9102 | ||
| Thermal conductivity (W/mK, at an average temperature of 20℃) | 60K | 80~100K | 110~160K | KS L 9016 |
| 0.037 | 0.035 | 0.035 | ||
| Combustion feature | Non-combustible material | IMO Res. MSC 307(88)-(2010 FTP Code) | ||
| Surface flammability | Flame spread index : 0 | ASTM E 84 | ||
| Smoke generation index : 10 | ||||
| Division | ||
|---|---|---|
| Hot shrinkage temperature | ||
| Performance | Over 600℃ (10% contraction of thickness) |
|
| Test Method | KS L 9102 | |
| Thermal conductivity (W/mK, at an average temperature of 20℃) |
||
| Performance | 60K | 0.037 |
| 80~100K | 0.035 | |
| 110~160K | 0.035 | |
| Test Method | KS L 9016 | |
| Combustion feature | ||
| Performance | Non-combustible material | |
| Test Method | IMO Res. MSC 307(88)-(2010 FTP Code) |
|
| Surface flammability | ||
| Performance | Flame spread index : 0 | |
| Smoke generation index : 10 | ||
| Test Method | ASTM E 84 | |
Glass Wool
Non-combustibility, sound absorption, insulation performance, A-CLASS
. . .
This product is an inorganic artificial mineral fiber insulation produced by melting glass at a high temperature and making them fiber using a binder.
It is applied to keep the deck house warm and the LNG cargo container cool. It acquired official certifications as a non-combustible material from
domestic and international classification societies including the European society.
| Division | Performanc | Test Method | |||
|---|---|---|---|---|---|
| Hot shrinkage temperature | Over 300℃ (10% contraction of thickness) | KS L 9102 | |||
| Thermal conductivity (W/mK, at an average temperature of 20℃) | 24K | 32K | 40K | 48K | KS L 9016 |
| 0.035 | 0.034 | 0.034 | 0.034 | ||
| Combustion feature | Non-combustible material | IMO Res. MSC 307(88)-(2010 FTP Code) | |||
| Surface flammability | Flame spread index : 0 | ASTM E 84 | |||
| Smoke generation index : 10 | |||||
| Division | ||
|---|---|---|
| Hot shrinkage temperature | ||
| Performance | Over 300℃ (두께 10% 수축) |
|
| Test Method | KS L 9102 | |
| Thermal conductivity (W/mK, at an average temperature of 20℃) |
||
| Performance | 24K | 0.035 |
| 32K | 0.034 | |
| 40K | 0.034 | |
| 48K | 0.034 | |
| Test Method | KS L 9016 |
|
| Combustion feature | ||
| Performance | Non-combustible material | |
| Test Method | IMO Res. MSC 307(88)-(2010 FTP Code) | |
| Surface flammability | ||
| Performance | Flame spread index : 0 | |
| Smoke generation index : 10 | ||
| Test Method | ASTM E 84 | |